Hydrothermal stability of NaBH₄ enclathrated sodalites with aluminosilicate and gallosilicate framework

verfasst von

Josef Christian Buhl, Florian Stemme, Irma Poltz

Abstract

The time dependent stability of tetrahydroborate sodalites with aluminosilicate- and gallosilicate framework was studied in water at room temperature and under hydrothermal conditions at 353 K. The experiments were carried out in different time intervals (4-48 h) using an excess of water according a solid:liquid mass ratio of 1:150. The kinetics of decomposition was followed by registration of weight loss, change of the pH-value and by X-ray powder diffraction as well as FT-IR spectroscopy. Both samples undergo remarkable time dependent decomposition. The decomposition rate is higher for the gallosilicate sodalite even though its crystal size is larger compare to the aluminosilicate sodalite. Besides formation of some X-ray amorphous material in both cases precipitation of crystalline aluminosilicate or gallosilicate was found, always connected with impurities of carbonate anions. FT-IR clearly showed that the remaining parts of sodalite structure of both samples were always pure tetrahydroborate sodalite. No borate species other than BH₄^- were detected. Thus, hydrolysis of the moisture sensitive BH₄^- anions by an entrance of water into intact cages can be excluded under the described experimental conditions.

Organisationseinheit(en)

Institut für Mineralogie

Typ

Artikel

Journal

Microporous and Mesoporous Materials

Band

126

Seiten

276-282

Anzahl der Seiten

7

ISSN

1387-1811

Publikationsdatum

12.2009

Publikationsstatus

Veröffentlicht

Peer-reviewed

Ja

ASJC Scopus Sachgebiete

Allgemeine Chemie, Allgemeine Materialwissenschaften, Physik der kondensierten Materie, Werkstoffmechanik

Elektronische Version(en)

https://doi.org/10.1016/j.micromeso.2009.06.018 (Zugang: Geschlossen)