High-pressure study on dioxolane silica sodalite (C₃H₆O₂)₂[Si₁₂O₂₄] - neutron and X-ray powder diffraction experiments

verfasst von

K. Knorr, C. M. Braunbarth, G. Van De Goor, Peter Behrens, C. Griewatsch, W. Depmeier

Abstract

Neutron and X-ray high-pressure powder-diffraction experiments on silica sodalite with 1,3-dioxolane as a template molecule, (C₃H₆O₂)₂[Si₁₂O₂₄], were performed up to a maximum pressure of 2.7 GPa. A phase transition from the fully expanded structure at ambient pressure, space group Im3̄m, to the acentric space group I4̄3m was derived from the observed compression behaviour. A ferro-elastic phase transition appears at about 1.2 GPa to the rhombohedral crystal system. From symmetry analysis and the observed transition behaviour the space groups R3 or R3m are proposed for p>1.2 GPa.

Organisationseinheit(en)

Institut für Anorganische Chemie

Externe Organisation(en)

Helmholtz-Zentrum Berlin für Materialien und Energie GmbH
Universität Konstanz
Christian-Albrechts-Universität zu Kiel (CAU)

Typ

Artikel

Journal

Solid state communications

Band

113

Seiten

503-507

Anzahl der Seiten

5

ISSN

0038-1098

Publikationsdatum

27.01.2000

Publikationsstatus

Veröffentlicht

Peer-reviewed

Ja

ASJC Scopus Sachgebiete

Chemie (insg.), Physik der kondensierten Materie, Werkstoffchemie

Elektronische Version(en)

https://doi.org/10.1016/S0038-1098(99)00516-5 (Zugang: Unbekannt)